Started with 2 layer of nested crystal structures, how many layers can we weave/build? More than two layers seem like a natural/infer progression. Visual confirmation of each additional layer will be challenging because of each subsequent layer will be smaller than outer layer/shell.

Clever/creative/innovative ht nesting cycles could build deeper than 2 layer of nesting structures by cyclical temperature manipulation. 3rd layer may sees small increase in hrc (0.5-1 point) due to more RA -> Mart conversion. 4th layer probably sees less than 0.25rc increase. Could be that after 2nd or 3rd or 4th be diminishing return value. That’s true, when performance gain is less than noise/deviation/error.